After coated with catalysts, this product is applied in catalytic converter of gasoline vehicle to catalyze, convert and purify the exhaust, making vehicle exhaust reaching standards of Euro IV and Euro V.
Item |
Standard value |
Tolerance range |
Remark |
wall thickness |
0.17MM |
+0.03MM -0.02MM |
|
density scope |
440g/L |
±60g/L |
|
Outside dimension |
≤100MM |
±1MM |
|
>100MM |
±1% |
|
|
Perpendicularity |
≤100MM |
≤1%height |
|
Parallelism |
>100MM |
≤1%height |
|
Item |
Standard value |
Inspection Method |
|
chemical components |
Al2O3 |
35.2±1% |
Chemical analysis |
SiO2 |
50.9±1% |
||
MgO |
13.9±1% |
||
Cordierite Crystal phase |
≥90% |
X-ray diffraction techniques |
|
Compressive strength |
AA xis |
≥15 Mpa |
Compressive strength technique |
BA xis |
≥2 Mpa |
||
CA xis |
≥0.15 Mpa |
||
Water absorption |
20-26%
|
Weighting methord |
|
Softening point |
≥1400 |
High temperature oven |
|
CTE(800℃) |
≤1.2*10-6/℃ |
Netzsch dil 402 PC |
|
Thermal shock resistance |
550℃three times(air cool) |
Muffle furnace |
Cell density (CPSI):100~600 |
||||
Item |
(mm) Sectional Dimension |
(mm2) Area of Section |
Shape of Section |
(mm) Height |
1 |
Φ76.2 |
4560 |
≤200 The height can be designed by customer (The standard height):76.2mm(3”), 101.6mm(4”), 127mm(5”), 152.4mm(6”). |
|
2 |
Φ83 |
5410 |
|
|
3 |
Φ93 |
6793 |
|
|
4 |
Φ97 |
7390 |
|
|
5 |
Φ101.6 |
8107 |
|
|
6 |
Φ103 |
8332 |
|
|
7 |
Φ105.7 |
8775 |
|
|
8 |
Φ118.4 |
11010 |
|
|
9 |
Φ144 |
16286 |
|
|
10 |
80x57(R21.5) |
3546 |
|
|
11 |
99.5x68.1(R33.6) |
5758 |
|
|
12 |
120.6x80(R39.6) |
8227 |
|
|
13 |
144x68(R28.4) |
8194 |
|
|
14 |
144.3x68.1(R28.4) |
8606 |
|
|
15 |
144.8x81.3(R37) |
9922 |
|
|
16 |
147x95(R36.6) |
11010 |
|
|
17 |
148x84(R38) |
10438 |
|
|
18 |
169.7x80.8(R37.2) |
11865 |
|
|
19 |
Triangle 143.5×84 |
9108 |
|
|
20 |
Trapezium 112.2×92×152.4 |
8788 |
|
|
21 |
Trapezium 122.3x104.4 |
10336 |
|
|
22 |
Rectangle 119.5x99.5 |
10529 |
|
|
23 |
Special 114x105 |
9612 |
|